Design and manufacturing of thermoplastic curved fuselage panel for Large Passenger Aircraft

1. Introduction

The application of technologies as automatic laying-up with composite materials helped to reduce production times and costs [1]. In the case of thermoplastic composites, the automatic laying-up process requires to increase the temperature to the matrix melting point, then, the incoming material and the substrate are bonded together under the force of a compaction roller. The main advantage of this process is the suppression of autoclave or oven secondary cycles, the part after laminating is finished for inspection [2]. The complexities associated to this process are delaying its application to the industry, making necessary to conduct detailed studies of all the physics interacting in the process: thermal transferences [3], degradation [4], crystallization [5], voids collapse or migration and residual stresses.

2. Materials

The material used for manufacturing the stiffeners and the skin was Toray Cetex TC1225 PAEK, with standard modulus carbon fiber T700. For hand lay-up activities (stiffeners), 194gsm material in the format of 12’’ width, was selected. For automatic laying-up (skin), 134gsm material in the format of ¼’’ width was chosen.

As explained below, the part includes reinforced patches. The material used for manufacturing the reinforcements wasHEXCEL AGP-193-PW/8552 RC40.

3. Design

The design of the stacking sequence and the geometry of this demo was calculated by using the results obtained after testing several coupons extracted from a flat demonstrator (skin reinforced with omega stringers and Z frame): filled-hole tension, open-hole compression, bearing, crippling, unfolding and mouse hole tests, conducted by Elements [6].

FIDAMC oversaw manufacturing the flat demo [7] in cooperation with Aernnova.

Figure 1 shows the curved part design where the green areas represent the thermoset reinforcements. The part had simple curvature with a radii of 3000mm and 1300x1150mm global dimension.

Figure 1 Geometry and dimensions of the curved demo

This curved demo was tested under typical fuselage loads, combining shear and pressurization.

4. Manufacturing

Different technologies were used for manufacturing the stiffeners and the skin.

4.1. Stiffeners

Four omega stringers were manufactured by hand lay-up and hot plate press forming by using a dedicated tooling. Two Z-shape frames were manufactured by hand lay-up and hot plate press forming by using a dedicated tooling. A hot plate press from Marzola-Biele Group was used.

One press cycle was used to consolidate each omega stringers, unlike the frames, which needed a first cycle to form the geometry and a secondary one to consolidate.

The stiffeners were located into the cavities of a lamination tooling, specifically designed for this purpose. Each omega stiffener hosted in its cavity two metallic modules to allow lamination, maintaining the shape, and helping to demold. Each Z shape frame hosted a metallic modulus on one side. None of the stiffeners had fillers, the metallic modules were designed to be adapted to these areas.

None of the modulus was self-heated, although the rest of the tool was heated by electrical resistances distributed in the whole area, generating important heterogeneities in the lamination area.

4.2. Skin

The skin was automatically laminated by using a gantry style machine from the Spanish supplier MTorres. Six tows of ¼’’ were placed by heating with a diode laser. Figure 2 shows the tooling before placing the stiffeners (a), the stiffeners after positioning (b) and the lamination process (c & d).

Complete laying-up process was done with self-heated tooling at 200 ⁰C to compensate and prevent from thermal residual stresses. The heterogeneous behavior of the tooling, the stiffeners, and the metallic modulus in terms of temperature highly impact in the thermal distortions experienced by the external metallic modulus and the demonstrator.

(a)	(b)
(c)	(d)

Figure 2 Curved demo during manufacturing.

4.3. Packers

With the purpose of part testing, different areas of the demo were reinforced by bonding patches of thermoset composite material. The patches were cured with the curved shape in oven using vacuum bag and then bonded to the thermoplastic composite demonstrator by using an adhesive film.

Figure 3 Curved demo after trimming.

Conclusions

A fuselage panel with thermoplastic composite materials was obtained by press forming and automatic laying-up. After non-destructive inspection, good quality was demonstrated in the whole skin panel and in the bonding lines: frames-skin and stringers-skin, which manifest the capabilities of this process to consolidate the skin and weld the skin and the stiffeners. Nevertheless, to permit the industrial scale up of the process, the speed should be improved, and the thermal distortions need to be re-evaluated.

Considering heat transference, a deep study should be conducted to check the impact of isolative or conductive materials in the tooling.

The tests conducted on the final demo demonstrated that the requirements predicted by simulation based on flat panel tests, were fulfilled.

Acknowledgment

This work was supported by the Large Passenger Aircraft (LPA GAM 2019) project [grant number 807097]. The authors would like to thank the European Commission for their financial assistance and for promoting cooperation between research and industry across Europe.

Bibliografía

[1]	A. Crosky, C. Grant, D. Kelly, X. Legrand y G. Pearce, «Fibre placement processes for composites manufacture,» Advances in composites manufacturing and process design, pp. (pp. 79-92), 2015. DOI:10.1016/B978-1-78242-307-2.00004-X
[2]	Z. Qureshi, . T. Swait, R. Scaife y H. El-Dessouky, «In situ consolidation of thermoplastic prepreg tape using automated tape placement technology: Potential and possibilities.,» Composites Part B: Engineering, vol. 66, pp. 255-267, 2014. DOI:10.1016/j.compositesb.2014.05.025
[3]	A. Zaami, M. Schäkel, I. Baran, T. C. Bor, H. Janssen y R. Akkerman, Journal of Composite Materials, vol. 55, nº 8, pp. 1073-1090, 2021. DOI: 10.1177/0021998320944598
[4]	I. Martín, F. Rodríguez-Lence, A. Güemes, A. Fernández-López, L. A. Pérez-Maqueda y A. Perejón, «On the determination of thermal degradation effects and detection techniques for thermoplastic composites obtained by automatic lamination,» Composites Part A: Applied Science and Manufacturing, vol. 111, pp. 23-32, 2018. DOI:10.1016/j.compositesa.2018.05.006
[5]	C. Zhang, Y. Duan, H. Xiao, B. Wang, Y. Ming, Y. Zhu y F. Zhang, «Effect of porosity and crystallinity on mechanical properties of laser in-situ consolidation thermoplastic composites,» Polymer, vol. 242, p. 124573, 2022. DOI:10.1016/j.polymer.2022.124573
[6]	K. Muñoz, M. Jiménez, M. J. Mesa, R. Cabrera, S. Anaya, R. Elices, K. Fernández y J. Cuenca, «Allowables Evaluation for the Design of a Thermoplastic Fuselage,» de XIV CONGRESO NACIONAL DE MATERIALES COMPUESTOS, Sevilla, 2022. DOI: 10.5281/zenodo.7603040
[7]	I. Martin, K. Fernández, J. Cuenca, C. Sánchez, S. Anaya y R. Élices, «Design and manufacture of a reinforced fuselage structure through automatic laying-up and in-situ consolidation with co-consolidation of skin and stringers using thermoplastic composite materials,» Heliyon, vol. 9, nº 1, 2023. DOI:10.1016/j.heliyon.2022.e12728