Comparison Between Parameters of Corrosion, Obtained by Destructive and Non-destructive Electrochemical Techniques

Abstract

This research aims to compare corrosion parameters obtained by linear polarization technique and Tafel extrapolation method in steel bars embedded in concrete. It was analyzing the intervention of mineral additions, such as metakaolin (10%) in binary concrete mixtures and silica fume (9% ) and nano silica (1%) in ternary concrete mixtures of water/binder ratio of 0.4 and 0.6 after induction of corrosion by wetting and drying cycles in a solution containing chlorides. Thus, the corrosion potential (Ecorr), polarization resistance (Rp) and corrosion rate (icorr) were measured. As a main result, a good correlation (R² of 0.82 and 0.96) was obtained with the values of polarization resistance (Rp) and corrosion rate (icorr), obtained by Rp and by Tafel slope, respectively. Binary and ternary concretes mixtures showed higher performance than reference concretes. Reference concrete with w/ratio of 0.6 showed a high corrosion rate.