In this study, the impact of the thaumasite sulfate attack (TSA) on cement mortar was investigated by comparing it to the ettringite sulfate attack (ESA). Mortar specimens with three binders, corresponding to the blank, ESA, and TSA, were exposed to sulfate solution. The evolutions of thaumasite and ettringite formation, pore structure, and gas permeability on the mortar specimens were characterized through XRD, 1H NMR, and CemBureau device. The experimental results show that: (1) both ettringite and thaumasite were formed in TSA; (2) ESA reduces the capillary pore space, whereas TSA decreases both the capillary pore and interlayer pores; and (3) ESA decreases the gas permeability while TSA significantly increases it. | In this study, the impact of the thaumasite sulfate attack (TSA) on cement mortar was investigated by comparing it to the ettringite sulfate attack (ESA). Mortar specimens with three binders, corresponding to the blank, ESA, and TSA, were exposed to sulfate solution. The evolutions of thaumasite and ettringite formation, pore structure, and gas permeability on the mortar specimens were characterized through XRD, 1H NMR, and CemBureau device. The experimental results show that: (1) both ettringite and thaumasite were formed in TSA; (2) ESA reduces the capillary pore space, whereas TSA decreases both the capillary pore and interlayer pores; and (3) ESA decreases the gas permeability while TSA significantly increases it. | ||
| + | |||
| + | == Full Paper == | ||
| + | <pdf>Media:Draft_Sanchez Pinedo_156331128108.pdf</pdf> | ||
Revision as of 11:27, 3 October 2023
Abstract
In this study, the impact of the thaumasite sulfate attack (TSA) on cement mortar was investigated by comparing it to the ettringite sulfate attack (ESA). Mortar specimens with three binders, corresponding to the blank, ESA, and TSA, were exposed to sulfate solution. The evolutions of thaumasite and ettringite formation, pore structure, and gas permeability on the mortar specimens were characterized through XRD, 1H NMR, and CemBureau device. The experimental results show that: (1) both ettringite and thaumasite were formed in TSA; (2) ESA reduces the capillary pore space, whereas TSA decreases both the capillary pore and interlayer pores; and (3) ESA decreases the gas permeability while TSA significantly increases it.
Full Paper
Document information
Published on 03/10/23
Submitted on 03/10/23
DOI: 10.23967/c.dbmc.2023.108
Licence: CC BY-NC-SA license
Share this document
Keywords
claim authorship
Are you one of the authors of this document?