Abstract
Crack tip opening angle (CTOA) is becoming one of the more widely accepted properties for characterizing fully plastic fracture. In fact, it has been recognized as a measure of the resistance of a material to fracture, in cases where there is a large degree of stable-tearing crack extension during the fracture process. This type of steady-state fracture resistance takes place when the CTOA in a material reaches a critical value, as typically occurs in low-constraint configurations. Our current research has applied the CTOA concept as an alternative or an addition to the Charpy V-notch and the drop weight tear test (DWTT) fracture energy in pipeline characterization. A test technique for direct measurement of CTOA was developed, using a modified double cantilever beam (MDCB) specimen. A digital camera and image analysis software are used to record the progression of the crack tip and to estimate CTOA using the crack edges adjacent to the crack tip. A steady-state CTOA has been successfully measured on five different strength grades of gas pipeline steel (four low strength grades and one high strength grade: X100). In addition, two-dimensional finite element models (2D FEMs) are used to demonstrate the sequence of the fracture process and the deformation mechanisms involved. The CTOA measurements and models are correlated and agree well.Copyright © 2006 by ASME
Original document
The different versions of the original document can be found in:
Document information
Published on 01/01/2006
Volume 2006, 2006
DOI: 10.1115/ipc2006-10172
Licence: CC BY-NC-SA license
Share this document
Keywords
claim authorship
Are you one of the authors of this document?