Steel in contact with fresh concrete is covered by a layer of passivating oxydes due to the alkaline nature of the pore solution. The presence of oxygen plays an important role in this passivation process as well as in the corrosión one when is developped due to the ingress of aggressives, such as, chioride ions. In the present paper, results are commented on the behaviour found when oxygen is limited due to the concrete curing conditions, in a completely saturated chamber. Surprisely, the results indícate that the oxygen availability during the curing has a marked influence on the future corrosión beabieviour This allows to deduce that the mechanisms involved are not so simple as was currently accepted and that new specific tests are needed to clarify the controversial points.

Resumen

Cuando el acero se pone en contacto con el hormigón fresco, debido a la naturaleza alcalina de éste, el acero se recubre de una capa de óxidos pasivantes, que lo mantienen constantemente protegido. En este proceso juega un papel preponderante la presencia del oxígeno, que resulta también esencial para el desarrollo de los procesos de corrosión, cuando hay agresivos presentes (por ejemplo los cloruros). En el presente trabajo se comentan resultados de los cambios que se aprecian, tanto en el proceso de pasivación como de corrosión, cuando el acceso de oxígeno se limita, circunstancia que se produce cuando el hormigón se cura en condiciones de saturación de agua. Los resultados muestran que la disponibilidad de oxígeno durante el curado tiene una marcada influencia en la resistencia futura a la corrosión lo, que indica que los mecanismos no son tan evidentes como se pensaba y se necesitarán ensayos futuros específicos para aclarar todos los aspectos que ahora aparecen como contradictorios.

Full Document